() may occur in weldments of QTLA steels after welding if cooling rate is too slow.
A. auto-tempering
B. upper bainite
C. M-A constituents
D. softening
E. 2-2-2
F. 期末
查看答案
High content of vanadium possibly increase susceptibility of HTLA steels to ().
A. hydrogen induced cracking
B. reheat cracking
C. softening
D. solidification cracking
E. 2-3-2
F. 期末
Normally, we'd better pay more attention to hydrogen induced cracking when () are welded by SMAW.
A. plain high carbon steels
B. QTLA steels
C. HTLA steels
D. plain low carbon steels
E. 2-1-2 2-2-2 2-3-2
F. 期末
Effects of Mo in HTLA steels include ().
A. improving hardenability
B. improving tempering stability
C. decreas grain size
D. decreas temper embrittlement
E. 2-3-1
F. 期末
Welding concerns of HTLA steels include ().
A. hydrogen induced cracking
B. reheat cracking
C. toughness decrease
D. solidification cracking
E. 2-3-2
F. 期末